Ferro Aluminum & Alloys
FERRO ALUMINIUM
Aluminium finds its use as one of the most commonly & preferred Deoxidizer in Steel making. Steelmakers have always been skeptical with respect to the efficiency & recovery of Aluminium Ingots or wire additions for both cost and quality reasons.
Hence the introduction of Ferro Aluminium was made to overcome this problem. With density of Ferro Aluminium estimated close to 4‐5gm/cm3as compared to that of liquid steel (7 gm/cm3), it dissolves & penetrates to the bottom of ladle or furnace thereby giving complete recovery & uniform treatment.
Grade Table
| GRADES | AL% | C% | SI% | MN% | S & P% | FE% |
|---|---|---|---|---|---|---|
| FeAl 300 | 30‐35% | 0.10% | 0.30% | 0.03% | 0.03% | Balance |
| FeAl 350 | 35‐40% | 0.10% | 0.30% | 0.03% | 0.03% | Balance |
| FeAl 600 | 60% | 0.15% | 0.50% | 0.50% | 0.03% | Balance |
Apart from the above standard grades, Ferro Aluminium can be manufactured as per the required specifications and sizes based on their applications. (25%; 40%; 50%; 55%; 70%)
Other Specifications
- Size: 4x4x3 cm Piglets, 6x6x3 cm Piglets, 9x8x7 cm Piglets
- Packing: In 50 kg Double Gunny Bags; or Jumbo Bags (1000 kg ); Steel Drums ( As per requirement)
- Appearance: Greyish Silver
- Specific density:4‐5gm/cm3
- Melting point:1200‐1300oC
NICKEL MAGNESIUM
Nickel Magnesium Alloys are Master Alloys of Magnesium with Nickel, which facilitates higher transfer of Magnesium into the liquid Cast Iron in comparison with pure magnesium due to metal density variations of liquid Iron & Magnesium. Additions of NiMg into liquid Iron promote Nodular Graphites in Ductile Iron.
Other Specifications
- Size: Lumps : 10‐60 mm or 5‐80 mm (As required)
- Packing: In Steel Drums
- Bulk Density: 7.8‐7.9g/Cm3
- Melting Point: 1300‐1320oC
Grade Table
| GRADES | NI | MG | RE | FE |
|---|---|---|---|---|
| Pyro NiMag 50 | Balance | 4‐5% | With or without | 1% Max |
| Pyro NiMag 160 | Balance | 14‐16% | With or without | 1% Max |
| Pyro NiMag 200 | Balance | 18‐20% | With or without | 1% Max |
(Other grades available & can be manufactured as per specific requirements & applications)
FERRO TITANIUM
Ferro Titanium has been used for many years as an additive in steel making. The excellent strength‐to‐weight ratio makes the alloy ideal for applications in the aerospace & automobile industry
Other Specifications
- Size: Lumps : 10‐60 mm or 5‐80 mm (As required)
- Packing: In Jumbo Bags or Drums
Grade Table
| GRADES | Ti | Al | Si | C | S & P | FE |
|---|---|---|---|---|---|---|
| FeTi 70% | 70% | 1% | 2% | 0.10% | 0.03% | Balance |
| FeTi 65% | 65% | 4% | 10% | 0.10% | 0.03% | Balance |
| Thermit 30% | 30-35% | 9% | 3% | 0.10% | 0.03% | Balance |
(Other grades available & can be manufactured as per specific requirements & applications)
FERRO MOLYBDENUM
Other Specifications
- Size: Lumps : 10‐50 mm
- Packing:In Steel Drums
Other Alloys include: Low/Medium Carbon Ferro Manganese, Ferro Nickel, Copper Magnesium
Grade Table
| GRADES | MO% | C% | SI% | S & P% | AL% | FE% |
|---|---|---|---|---|---|---|
| FEMO 57% | 57% | 0.10% | 2% | 0.05% | 0.50% | Balance |
| FEMO 60% | 60% | 0.10% | 2% | 0.05% | 0.50% | Balance |
ALUMINIUM DE-OXIDISERS
(PIGLETS/ SHOTS/ NOTCH BARS)
Aluminium Piglets Shots & Notch Bars are used in Steel Plants for De Oxidation, Removing Oxidation Skin, Eliminating Surface Defects, Removing Stress, Strengthen, Precision Casting, Automobile Spare, and Pump Valve Industry.
Other Specifications
- Al: 96% ‐ 97% Min; C: 0.10% Max; Cu: 0.30% Max; Mn:0.30% Max; Mg:0.50% Max; Si: 0.50% Max; Fe:1% Max
- Size: